Polymerizing unsaturated monomers with a catalyst of an iron complex, a dialkyl aluminum compound and a bidentate ligand

ABSTRACT

Process for polymerizing olefins, diolefins and alkylene oxides in the presence of a catalyst system comprised of an iron complex, a trialkyl aluminum compound and a bidentate ligand capable of both p i ( pi and sigma ( sigma ) banding to form a five or six-membered ring.

United States Patent Bozik et a].

[151 3,678,022 [451 July 18,1972

[72] Inventors: John E. Bozik, Pittsburgh; Harold E. Swift, Gibsonia; Ching Yong WufPittsburgh, all

of Pa.

[73] Assignee: Ameripol, Inc.

[22] Filed: July 9, 1970 [21] Appl.No.: 61,011

Related US. Application Data [62] Division of Ser. No. 812,536, March 10, 1969, Pat.

[52] US. Cl. ..260/88.7, 252/43 l 260/2, 260/82.l, 260/85.5, 260/87.5, 260/87.7, 260/9l.7,

51 Int. Cl ..c0sr3/22, com/74 58 new ofSearch ..260/9l.7, 92.1, 92.8, 88.7

[56] References Cited UNITED STATES PATENTS 3,565,875 2/1971 Bozik et a1 ..260/94.3

Primary Examiner-Harry Wong, Jr. Attorney-J. Hughes Powell, Robert W. Wilson and Ernest K. Bean 57 ABSTRACT Process for polymerizing olefins, diolefins and alkylene oxides in the presence of a catalyst system comprised of an iron complex, a trialkyl aluminum compound and a bidentate ligand capable of both p i (want! sigma (a) banding to form a five or six-membered ring.

9 Claims, No Drawings POLYMERIZING UNSATURATED MONOMERS WITH A CATALYST OF AN IRON COMPLEX, A DIALKYL ALUMINUM COMPOUND AND A BIDENTATE LIGAND This is a division of application Ser. No. 812,536 filed Mar. 10, 1969, now US. Pat. No. 3,565,875 issued Feb. 23, 1971.

BACKGROUND OF THE INVENTION This invention relates to the polymerization of certain olefins, diolefins and alkylene oxides. More specifically, this invention relates to the rapid, relatively low temperature polymerization of a wide variety of organic monomers in high yields employing a highly specific three component catalyst system.

Many catalyst systems heretofore employed have been limited in their applicability due to their inability to catalyze polymerization activity in a variety of different monomers. Instead, most catalyst systems are employed to aid in the polymerization of a highly specific and narrow class of monomers. The restricted applicability of such catalyst systems severely limits the flexibility and range of commercial plant operations.

Specifically, coordination catalysts are generally limited in their ability to polymerize either polar or non-polar monomers. Few, if any, coordination catalysts are known to polymerize both polar and non-polar monomers. In addition, although coordination catalysts generally consist of at least one metallic component, few, if any, of such catalysts have heretofore been employed to obtain high molecular weight polymer employing an iron compound as a metallic compound. Iron compounds, though stable, inexpensive and readily available have basically been relegated as catalyst components to oligomerization.

Accordingly, it is an object of the present invention to provide a catalyst system and polymerization process capable of polymerizing a wide variety of organic monomers.

It is another object to provide a coordination catalyst system and polymerization process capable of polymerizing both polar and non-polar monomers.

It is still another object to provide a coordination catalyst system employing an iron complex as one of the components thereof.

SUMMARY OF THE INVENTION These, as well as other objects, are accomplished in accordance with the present invention which provides a process comprising polymerizing monomers selected from the group consisting of:

a. olefins having the formula:

H C CR,R wherein R can be a halogen or an alkyl group containing from one to four carbon atoms and R can be a halogen or a cyano radical;

b. diolefins; and

c. alkylene oxides having the formula:

wherein R is hydrogen or an alkyl or aryl group containing from one to about six carbon atoms; in contact with a catalytically effective amount of a catalyst system comprising:

i. an iron complex comprising a ligand containing oxygen donor atoms;

ii. a trialkyl aluminum compound; and

iii. a bidentate ligand capable of both pi and sigma bonding to form a five or six-membered chelate ring, characterized by the structural formula:

Lil.

wherein m is a number from 0 to l, x is a number from 0 to 1, Y is a number from 0 to 4, R is a radical selected from the group consisting of hydrogen, alkyl, aryl, halogen, hydroxyl and acetoxy, and Q is a radical selected from the group consisting of hydrogen, alkyl, halogen, hydroxyl and acetoxy, the major portion of said sigma bonding being attributable to the ring nitrogen.

DESCRIPTION OF THE INVENTION The catalyst system of the present invention is useful in polymerizing a wide variety of monomers both polar and nonpolar. For example, monomers which are polymerizable in accordance with the present invention are exemplified by:

a. olefins having the formula:

wherein R can be a halogen such as chlorine, bromine, iodine and fluorine or an alkyl group containing from one to about four carbon atoms such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, tert.-butyl and the like, and R can similarly be a halogen or a cyano radical. Illustrative of such olefins are vinylidene chloride, methacrylonitrile, vinylidene fluoride and the like;

b. diolefins especially the aliphatic acyclic conjugated diolefins containing from about four to about 12 carbon atoms such as butadiene, isoprene, piperylene, 2,3-dimethyl-butadiene, 1,3-pentadiene, chloroprene and the like; and

c. alkylene oxides having the formula:

wherein R is an alkyl or aryl group containing from one to about six carbon atoms such as methyl, ethyl, propyl, butyl, phenyl and the like, or hydrogen. For example, ethylene oxide, propylene oxide, styrene oxide and the like have been found suitable.

In addition, the catalyst system of the present invention has been found useful in preparing copolymers of the various monomers set forth hereinabove. Surprisingly, although vinyl aromatics such as styrene were found to be inactive with the catalyst system of the present invention, they were found to copolymerize with the monomers set forth above.

Polymerization is obtained in accordance with the present invention by contacting at least one of the monomers described hereinabove with the three component catalyst system of the present invention in an inert diluent, if desired (although the use of such diluent is not considered necessary) at relatively low temperature, generally ranging from about '5()C. to about C. The polymerization proceeds rapidly resulting in high yields of polymer.

The catalyst system is a three component system comprismg:

i. an iron complex comprising a ligand containing oxygen donor atoms such as, for example, iron (III) acetylacetonate, iron (III) naphthenate, iron octoate and the like;

ii. a trialkyl aluminum preferably wherein the alkyl groups each contain from one to about eight carbon atoms, for example, methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, hexyl, octyl and the like. Illustrative of such compounds are triethyl aluminum, tri-isopropyl aluminum, tri-isobutyl aluminum, tri-n-butyl aluminum, tri-octyl aluminum and the like; and

iii. a bidentate ligand capable of both pi and sigma bonding to form a five or six-membered chelate ring, said ligand being characterized by the structural formula:

wherein R can be a radical such as hydrogen, alkyl, preferably alkyls containing from one to about eight carbon atoms such as methyl, ethyl, iso-propyl, tert.-butyl, hexyl, octyl and the like; aryl such as phenyl, benzyl and the like; halogen such as chlorine, bromine, iodine and fluorine; hydroxyl and acetoxy; Q can be a radical such as hydrogen, alkyl, preferably alkyls containing from one to about eight carbon atoms such as methyl, ethyl, iso-propyl, tert.-butyl, hexyl, octyl and the like, halogen such as chlorine, bromine, iodine and fluorine; m is a number from to l, x is a number from O to l and y is a number from 0 to 4.

Illustrative of the various ligands encompassed herein are the following examples which are not to be construed as imposing any limitation on the scope of the structural formula set forth hereinabove:

wherein R, Q and y are as defined above. Examples of such bidentate ligands are Z-cyanopyridine, phenyl-2- pyridylacetonitrile, 2-cyano-6-methylpyridine, 2-pyridinealdoxime and the like.

The three component catalyst system of the present invention is highly specific in that all three components must be present for the catalyst system to be active. In addition, it has been found that the requirements for each component are quite rigid. Many closely analogous materials for each catalyst component have proven inoperable or were found to result in extremely low yields of polymer or the formation of only dimers and trimers. For example, although iron acetylacetonate is a suitable iron complex, the following metal acetylacetonates M(AA), have proven inoperable: Ni(AA) Co(AA) Co(AA) Cr(AA) V(AA) Mn(AA) Zr(AA) Ce(AA) ,Cd(AA) and Zn(AA) In addition, although trialkyl aluminum compounds have proven suitable, other organometallic compounds have been found inoperable such as, for example, dialkyl aluminum halides, alkyl aluminum dihalides, phenyl magnesium chloride, di-sec-butyl magnesium and triethyl boron.

Still further, although many pyridine compounds and nitriles have proven to be suitable bidentate ligands, other closely analogous materials and even isomers have proven inoperable. For example, although Z-cyanopyridine is operable, 3-cyanoand 4-cyanopyridine have been found inoperable. Similarly, Z-aminomethyl pyridine, di-2-pyridyl ketone, 2- cyanoaniline, Z-acetyl pyridine, acetonitrile and 2-vinyl pyridine have been found inoperable.

It has been found in the present invention that in order to obtain an active polymerization catalyst, the ligand must be capable of coordinating with reduced iron in two positions, or function as a bidentate ligand. With 3 and 4-cyanopyridine, chelate rings cannot form and use of these compounds results in inactive systems.

hull

4-cyauopyridiuo .Z-cyanopyridine-iron inactive complex-uctivu Z-cyauopyridino inactive Although not wishing to be bound by any theory or mechanism, the relatively low activity ofthe Fe(AA) -,-TEA-2- cyano-6methyl-pyridine system strongly suggests a steric hindrance effect. The steric hindrance could be a physical blocking or interference ofthe incoming monomer.

Z-aminomethyl pyridine vinylpyridino Z-cyano-aniline The specificity of the ligand makes this catalyst system analogous to enzymatic action. The ligand must have side chain unsaturation to participate in d1r p11 bonding with the iron orbitals and stabilize the reduced valence state of iron. But yet the ligand has to have a donor atom in the side chain and in the aromatic ring to participate in mainly sigma bonding. Thus, it appears to be necessary to have a critical balance of 0' and 1r bonding in conjunction with stringent factors to have an active catalyst system.

Thus, it can readily be seen that the three component coordination catalyst of the present invention is highly specific with regard to the make-up of the three components.

The molar ratio of the trialkyl aluminum compound to the iron complex Al/Fe can be varied from about ill to about 4/1; however, higher yields of polymer can be obtained at Al/Fe ratios of from about 2.5 to about 3.5 with optimum yields being secured at ratios of about 3. The molar ratio of the bidentate ligand to the iron complex, ligand/Fe, can be varied from about 0.1/l to about 2.5/l with best results being obtained within the range of about 0.5 to about l.5. Small amounts of the catalyst system have been shown to be catalytically effective in the polymerization of the wide variety of monomers set forth hereinabove. For example, the molar ratio of monomer to iron complex, monomer/Fe, can vary from about /1 to about 400/1 without adverse effect on the rate of reaction or the efficiency ofpolymerization.

The polymerization reaction proceeds readily under normal conditions of temperature and pressure. The temperature can vary widely from about 50C. to about C; preferably and most conveniently, however, the reaction proceeds at or about room temperature (25C.). Although autogenous pressure developed during polymerization is generally sufficient, any pressure can be employed such as subatmospheric, atmospheric or superatmospheric. It is considered preferable that the reaction proceed under anhydrous conditions in an inert atmosphere such as under a blanket of nitrogen, argon, neon, and the like.

It is not considered necessary that an inert organic solvent or diluent be employed in the polymerization process; however, if desired, it has been found that the selection of the solvent is not critical and essentially any hydrocarbon solvent can be employed. The solvents can be aromatic, aliphatic or even halogenated hydrocarbons without adverse effect on the process. For example, solvents such as benzene, toluene, odichlorobenzene, n-hexane, heptane, 1,2-dichloroethane and the like have been found suitable. Preferably, aromatic hydrocarbon solvents are employed, such as benzene, toluene and the like, since these solvents have been found to provide a greater rate of polymerization.

Typically, the polymerization process proceeds in the following manner: to a dry 200 milliliter polymerization vessel is charged 0.] millimoles of iron acetylacetonate, 0.1 millimoles of phenyl-Z-pyridylacetonitrile, 40 milliliters of benzene, 20 milliliters (100 millimoles) of isoprene and 0.3 millimoles of triethyl aluminum in that order. The particular order of addition is not considered critical and can be altered, if desired. All reactants are kept under a dry nitrogen atmosphere at all times. The polymerization vessel is then sealed and the reaction is allowed to proceed with agitation at room temperature until completion. Generally, high conversions of about 75 percent are easily obtained within a relatively short period of time. The resulting polyisoprene cement is then poured into alcohol such as methanol, ethanol, or the like to coagulate the polymer. The resulting polymer is then dried and recovered.

The following examples are cited to further illustrate various embodiments of the present invention and should not be construed as imposing any restriction or limitation upon the scope or spirit of the present invention.

EXAMPLE 1 A 2,000 milliliter resin kettle equipped with a stirrer, nitrogen inlet and outlet, and a 250 milliliter addition flask was used as the reaction vessel. The kettle was thoroughly dried at l C. and allowed to cool to room temperature in a stream of dry nitrogen. The reactants were prepared in a nitrogen atmosphere in a glove box. To the resin kettle was added a solution of 4 millimoles of iron acetylacetonate, 4 millimoles of 2-cyanopyridine, 130 milliliters of benzene and 80 milliliters of isoprene. Thereafter, a solution of 12 millimoles of triethyl aluminum in 30 milliliters of benzene was added. A stream of nitrogen was kept flowing through the kettle at all times. When the reaction mixture became highly viscous, an additional 250 milliliters of benzene was added from the addition flask. The reaction was allowed to proceed for about 2 hours. The resulting polymer was then diluted with enough benzene to reduce the viscosity to a level where it would flow freely (about 500-] ,000 milliliters of benzene is generally sufficient for such purpose). Antioxidant was added to the solution. The dilute solution was then run into a methanol bath to coagulate the polymer. The recovered polymer was then dried in a vacuum oven. Infrared analysis established the polymer as being polyisoprene exhibiting the following microstructure: 50 percent cis-1,4, 3 percent trans-1,4, 2 percent 1,2 and 45 percent 3,4.

EXAMPLE 2 TABLE I Effect of Ligand on Yield of Polyisoprene Ligand Yield of Polymer 2-cyanopyridine 3-cyanopyridine 60 0 4-cyanopyridine 0 2-cyano-6-methyl-pyridine 2-pyridinealdoxime phenyl-Z-pyridylacetonitrile l ,2-bis-(2-pyridy1)-ethylene 2,2'-dipyn'dyl 2,2'dipyridylamine acetonitrile Z-cyanoaniline di-Z-pyridyl ketone Z-aminomethylpyridine Z-acetylpyridine 2-vinylpyridine EXAMPLE 3 Employing substantially the same procedure described in Example 1, several iron complexes were evaluated in lieu of the iron acetyl acetonate in the three component catalyst system for the polymerization of isoprene. Table II summarizes the results obtained:

TABLE II Effect of Iron Complex on Yield of Polyisoprene EXAMPLE 4 Employing substantially the same procedure described in Example 1, several transition metal acetylacetonates were evaluated in lieu of the iron acetylacetonate in the three component catalyst for the polymerization of isoprene. Table III summarizes the results obtained:

TABLE [II Effect of Transition Metal Acetylacetonates on Yield of Polyisoprene Metal Acetylacetonate (M(AA),) %Yield of Polymer EXAMPLE 5 TABLE IV Effect of Organometallic Reducing Agents on Yield of Polyisoprene Organometallic Compound Yield of Polymer triethyl aluminum (TBA) 60 tri-isobutyl aluminum 60 tri-octyl aluminum 60 diethyl aluminum chloride 0 ethyl aluminum dichloride 0 Employing substantially the same procedure described in Example 1, a wide variety of olefinic, diolefinic and alkylene oxide monomers were polymerized. Table V summarizes the results obtained:

TABLE V Monomer Conversion 7: Time (Hours) isoprene 75 2 butadicne-l,3 75 2 2,3-dimethyl-butadiene-l,3 60 2 pentadiene-l,3 50 2 vinylidene chloride 62 20 chloroprene 7 4 methacrylonitrile I5 20 propylene oxide 24 EXAMPLE 7 Employing substantially the same procedure as set forth in Example 1, butadiene was polymerized at 0C. in hexane solvent; a conversion of about 75 percent was achieved in about 2 hours. lnfrared analysis indicated a polybutadiene exhibiting the following microstructure: 14 percent trans-1,4; 33 percent cisl ,4 and 53 percent 1,2.

EXAMPLE 8 Employing substantially the same procedure described in Example 1, a mixture of isoprene and styrene (50 mole percent styrene) was charged to the polymerization vessel. The recovered copolymer was found to contain 18.6 mole percent styrene.

The polymers obtained in accordance with the present invention range from elastomeric polymers to plastics and resins. These polymers are useful in adhesives, belts, films, fibers, tire manufacture, electrical insulation and other similar uses.

What is claimed is:

1. Polymerization process comprising polymerizing monomers having the formula:

H C C R R wherein R can be a chlorine or fluorine or an alkyl group containing from one to about four carbon atoms, and R can be a chlorine or fluorine or a cyano radical;

in contact with a catalytically efiective amount of a catalyst system comprising:

i. an iron complex comprising a ligand containing oxygen donor atoms; ii. a trialkyl aluminum compound; and iii. a bidentate ligand capable of both pi and sigma bonding to form a five or six-membered chelate ring characterized by the structural formula:

Lil

wherein m is a number from 0 to l, is a number from 0 to I. Y is a number from 0 to 4, R is a radical selected from the group consisting of hydrogen, alkyl, aryl, halogen, hydroxyl and acetoxy, and Q is a radical selected from the group consisting of hydrogen, alkyl, halogen, hydroxyl and acetoxy, the major portion of said sigma bonding being attributable to the ring nitrogen. I

. Polymerization process as defined in claim 1 wherein the molar ratio of trialkyl aluminum to iron complex varies from about U] to about 4/1.

3. Polymerization process as defined in claim 1 wherein the molar ratio of bidentate ligand to iron complex varies from about 0. III to about 2.5/1.

4. Polymerization process as defined in claim 1 wherein the molar ratio of monomer to iron complex varies from about to about 400/1.

5. Polymerization process as defined in claim 1 wherein the polymerization is conducted at temperatures ranging from about 50C. to about C.

6. Polymerization process as defined in claim 1 wherein the polymerization is conducted in the presence of an inert or ganic solvent.

7. Polymerization process as defined in claim 6 wherein the solvent is an inert aromatic hydrocarbon solvent.

8. Polymerization process as defined in claim 1 wherein the catalyst system comprises (i) iron acetylacetonate, (ii) trialkyl aluminum, and (iii) 2-cyanopyridine.

9. Polymerization process as defined in claim 8 wherein phenyl-2-pyridylacetonitrile is employed in lieu of 2- cyanopyridine. 

2. Polymerization process as defined in claim 1 wherein the molar ratio of trialkyl aluminum to iron complex varies from about 1/1 to about 4/1.
 3. Polymerization process as defined in claim 1 wherein the molar ratio of bidentate ligand to iron complex varies from about 0.1/1 to about 2.5/1.
 4. Polymerization process as defined in claim 1 wherein the molar ratio of monomer to iron complex varies from about 100/1 to about 400/1.
 5. Polymerization process as defined in claim 1 wherein the polymerization is conducted at temperatures ranging from about -50*C. to about 150*C.
 6. Polymerization process as defined in claim 1 wherein the polymerization is conducted in the presence of an inert organic solvent.
 7. Polymerization process as defined in claim 6 wherein the solvent is an inert aromatic hydrocarbon solvent.
 8. Polymerization process as definEd in claim 1 wherein the catalyst system comprises (i) iron acetylacetonate, (ii) trialkyl aluminum, and (iii) 2-cyanopyridine.
 9. Polymerization process as defined in claim 8 wherein phenyl-2-pyridylacetonitrile is employed in lieu of 2-cyanopyridine. 